Sprayed powder coated aluminium panels are commonly used in the construction industry. Baked aluminium roofing sheet panels, also known as baked aluminium roofing sheet sheets, are a type of powder coated aluminium panel that has been baked.

A variety of industries, including construction, decoration, and transportation, use it because of its excellent corrosion and weather resistance, strength, and durability. It is also popular because of its beautiful appearance, ease of production when compared to anodic oxidation, and environmental protection, among other characteristics. It is also used in aerospace and defense.

Making the 5052 aluminum alloy substrate visible and creating a uniform activation surface before painting is critical to the quality of chromate conversion film and spraying quality of aluminum alloy profiles.



1.  Two baking fingers when spraying aluminum plate with three layers of coating

2.  Open three groups of guns and spray the first coat of primer, the second color paint (fluorine or polyester paint), the third coat of protective topcoat (varnish), two baking fingers when spraying heavy duty aluminum foil plate with three layers of coating

3.  When spraying painted aluminum company sheets plate with three layers of coating, two baking fingers when spraying aluminum plate with three layers of coating, two baking fingers when spraying aluminum plate with three layers of coating

4.  When spraying heavy duty aluminum foil plate with three layers ofHowever, the coating production line now primarily consists of three layers of baking, followed by two layers of coating baking, followed by three layers of baking

A common occurrence is for the surface of an aluminum veneer curtain wall to become contaminated. The application's scope is defined as follows:

In order to achieve this, it is necessary to use specialized paint on the canvas.

It has a variety of characteristics and is specifically designed for the surface of 5x10 aluminum sheet plate. Adhesion to 5x10  sheet plate is excellent; the paint film adheres to the 5052 aluminum plate and does not peel away from it, remaining firmly attached to the substrate. It is possible to use this product in conjunction with various metals including heavy duty aluminum foil, stainless steel, aluminum alloy, galvanized sheet, and other metals. Preventing sandblasting and sandblasting the substrate while only removing the surface oil layer, rather than completely removing the surface oil layer, will save you time and effort.

The fluorocarbon spray treatment is applied to the surface after the chroming and other pre-treatments have been completed. KANAR500 is a polyvinylidene fluoride resin that can be used as a topcoat and varnish for fluorocarbon coatings. Two, three, or four layers of coats are commonly used in the construction of coats. In addition to having excellent corrosion and weather resistance, fluorocarbon coatings are also resistant to acid rain, salt spray, and a variety of other airborne contaminants.

Cleaning the aluminium roofing sheet plate with solvent will help to remove oil and grease from the surface. After that, spray it with ED1000 epoxy primer in 1-2 coats, followed by a top coat after 24 hours of solid drying; the top coat should be chosen based on the actual environmental conditions. A pattern matching scheme that is frequently employed in practice.

In order to complete the electrostatic powder coating process, the following equipment must be utilized: electrostatic powder spraying equipmentPowder wikicoating /wikispraying to the surface of the workpiece results in a powder coating due to the electrostatic effect; powder coating after high-temperature baking leveling curing results in a final coating with different effects (different kinds of powder coating effect); patterned aluminum spraying effect in wikimechanical /wikistrength, adhesion, resistance to wikicorrosion/wiki, aging residuum results in a powder coating; powder coating after high-temperature

The following are the primary steps in the procedure:Oil removal, rust removal, phosphating, and passivation are some of the processes used. Using a pre-treatment, it is possible to produce a uniform and rough gray phosphate film on the workpiece. This film not only protects the surface from oil, rust, and dust, but it also helps to prevent rust and increases the adhesion of the spray layer to not only the original silver-white glossy surface, but also the original silver-white glossy surface.